Structures by: King H. W.

Total: 17

(Au Zn9)0.2

Au0.24Zn1.76

Massalski, T. B.King, H. W.

Acta Metallurgica (1962) 10, 1171-1181

a=2.8122Å   b=2.8122Å   c=4.3721Å

α=90°   β=90°   γ=120°

(Au3 Cd97)0.02

Au0.06Cd1.94

King, H.W.Farrar, R.A.

Metallography (1968) 1, 79-90

a=2.9811Å   b=2.9811Å   c=5.5389Å

α=90°   β=90°   γ=120°

(Au0.68 Cu0.12 In0.2)

Au0.68Cu0.12In0.2

Massalski, T.B.Isaacs, L.L.King, H.W.

Acta Metallurgica (1963) 11, 1355-1361

a=2.887Å   b=2.887Å   c=4.741Å

α=90°   β=90°   γ=120°

Au0.85Sn0.15

Au0.85Sn0.15

King, H.W.Massalski, T.B.

Acta Metallurgica (1960) 8, 677-683

a=2.9305Å   b=2.9305Å   c=4.7761Å

α=90°   β=90°   γ=120°

Silver cadmium (0.4/1.6)

Ag0.4Cd1.6

Massalski, T. B.King, H. W.

Acta Metallurgica (1962) 10, 1171-1181

a=3.0863Å   b=3.0863Å   c=4.8177Å

α=90°   β=90°   γ=120°

Silver cadmium (0.49/9.51) - HT

Ag0.495Cd0.505

Massalski, T.B.King, H.W.

Philosophical Magazine, Serie 8(1956-) (1961) 6, 669-682

a=2.9867Å   b=2.9867Å   c=4.8253Å

α=90°   β=90°   γ=120°

(Ag11 Hg9)0.1

Ag1.1Hg0.9

King, H.W.Massalski, T.B.

Philosophical Magazine, Serie 6 (1901-1925) (1961) 6, 669-682

a=2.9896Å   b=2.9896Å   c=4.8413Å

α=90°   β=90°   γ=120°

(Ag17 Sb3)0.1

Ag1.7Sb0.3

King, H.W.Massalski, T.B.

Philosophical Magazine, Serie 6 (1901-1925) (1961) 6, 669-682

a=2.9616Å   b=2.9616Å   c=4.799Å

α=90°   β=90°   γ=120°

Silver zinc (0.6/1.4)

Ag0.6Zn1.4

Massalski, T. B.King, H. W.

Acta Metallurgica (1962) 10, 1171-1181

a=2.8253Å   b=2.8253Å   c=4.471Å

α=90°   β=90°   γ=120°

Silver gallium (0.75/0.25)

Ag0.75Ga0.25

Massalski, T.B.King, H.W.

Journal of the Less-Common Metals (1991) 171, 157-162

a=2.8869Å   b=2.8869Å   c=4.6753Å

α=90°   β=90°   γ=120°

Silver tin (0.8/0.2)

Ag0.8Sn0.2

King, H.W.Massalski, T.B.

Philosophical Magazine, Serie 8(1956-) (1961) 6, 669-682

a=2.9658Å   b=2.9658Å   c=4.7842Å

α=90°   β=90°   γ=120°

(Mn Zn99)0.02

Mn0.02Zn1.98

Farrar, R.A.King, H.W.

Metallography (1970) 3, 61-70

a=2.6681Å   b=2.6681Å   c=4.9561Å

α=90°   β=90°   γ=120°

(Li Zn99)0.02

Li0.02Zn1.98

Farrar, R.A.King, H.W.

Metallography (1968) 1, 79-90

a=2.6655Å   b=2.6655Å   c=4.9467Å

α=90°   β=90°   γ=120°

(Mn0.52 Zn0.48)

Mn0.52Zn0.48

Farrar, R.A.King, H.W.

Metallography (1970) 3, 61-70

a=2.7339Å   b=2.7339Å   c=4.455Å

α=90°   β=90°   γ=120°

(Cd0.995 Mn0.005)

Cd0.995Mn0.005

Farrar, R.A.King, H.W.

Metallography (1970) 3, 61-70

a=2.9803Å   b=2.9803Å   c=5.6204Å

α=90°   β=90°   γ=120°

Cd0.8 Li0.2

Cd0.75Li0.25

Farrar, L.A.King, H.W.

Metallography (1968) 1, 79-80

a=3.9802Å   b=3.9802Å   c=5.6185Å

α=90°   β=90°   γ=120°

(Cu0.2 Zn0.8)

Cu0.2Zn0.8

Massalski, T. B.King, H. W.

Acta Metallurgica (1962) 10, 1171-1181

a=2.7418Å   b=2.7418Å   c=4.2939Å

α=90°   β=90°   γ=120°